Depends on the material. ABS would be a decent material for this application - as long as you have a decent enough setup to scrub / clean the air in the chamber / room.
PLA would have a hard time in that position, PETG might be OK, Nylon may creep after too many heat cycles. Depending on how hot those parts get this is.
Also, aren’t ovens hot? Won’t a 3d printed part melt straight away, or is there some special material?
Depends on the material. ABS would be a decent material for this application - as long as you have a decent enough setup to scrub / clean the air in the chamber / room.
PLA would have a hard time in that position, PETG might be OK, Nylon may creep after too many heat cycles. Depending on how hot those parts get this is.